Physical Properties |
Specification |
Size
(MM) |
Tensile Strength (Kg / mm2 )
Min |
% of Elongation 5.65
Min |
0.2% Proof Stress |
Hardness
HV |
IZOD
Impact Value
(Kg/FM) |
HT-1 IS 320/80 |
- |
49 |
12 |
- |
- |
- |
HT-2 IS 320/80 |
- |
53 |
12 |
- |
- |
- |
DIN EN 17660
MS 58
(Forging) |
- |
37 |
20 |
- |
- |
- |
BS 218
Modified
Forging Brass |
- |
40 |
18 |
- |
- |
2.2 |
DIN EN 17660
MS 58
(Free Cutting) |
- |
43 |
15 |
- |
- |
- |
Riveting Brass Wire (Leaded)
IS 2704/83 |
¼ Hard (HA)
½ Hard (HB)
Hard (HD)
Extra Hard (HE) |
325 Mpa
400 Mpa
500 Mpa
695 Mpa |
30
20
15
5 |
- |
110 to 130
131 to 150
151 to 175
176 to 215 |
- |
DIN EN 12164 CW 614N |
- |
43 |
10 |
- |
- |
- |
DIN EN 12164 CW 617N |
- |
43 |
10 |
- |
- |
- |
DIN EN 12164 CW 608N |
- |
40 |
25 |
- |
- |
- |
C 3601 JIS |
Annealed
½ Hard
Hard |
294 Mpa
343 Mpa
451 Mpa |
25
25
25 |
- |
- |
- |
C 3604 JIS |
- |
333 Mpa |
20 |
- |
- |
- |
C-3771 JIS |
- |
314 Mpa |
15 |
- |
- |
- |
CZ-112
Naval Brass Gr-1 |
Upto 12.50
12.50 to 50
50 to 100 |
40
38.50
35 |
18
18
18 |
- |
- |
- |
CZ-113
Naval Brass Gr-2 |
All Size |
40 |
15 |
- |
- |
- |
CZ-109
Lead Free |
- |
34 |
25 |
- |
- |
- |
CZ-108
Lead Free |
Annealed
Half Hard
Hard |
33
47 to 63
63 to 79 |
35
35
35 |
- |
- |
- |
CZ-114 |
Hard |
47
55 |
18
12 |
24.5
29.5 |
- |
- |
CZ-115 |
- |
47 |
20 |
19.50 |
- |
- |
CZ-121 |
Annealed 6 to 25
Annealed 25 to 50
Annealed 50 above
Half Hard 6 to 12
Half Hard 12 to 25
Half Hard 25 to 50
Half Hard 50 above
Hard 6 to 12
Hard 12 to 25 |
345 Mpa
315 Mpa
285 Mpa
405 Mpa
395 Mpa
355 Mpa
325 Mpa
550 Mpa
490 Mpa |
12
17
22
4
6
12
17
-
4 |
- |
- |
- |
CZ-122 |
- |
310 Mpa |
20 |
- |
- |
- |
CZ-124 |
6 to 12
12 to 25
25 to 50
50 above |
41
40
36
33 |
4
6
12
17 |
- |
- |
- |
CZ-130 |
- |
37 |
25 |
- |
- |
- |
CZ-131 |
- |
37 |
22 |
- |
- |
- |